Description
Scope and specifics of application
Polytex BS primer enhances the protective anti-corrosion properties of the complex coating. It is intended to prime metal structures in the industrial atmosphere of moderate-cold and cold climates exposed to vibration stress.
It is used to prime railway and urban transport, construction metal structures, oil and gas pipelines, tanks, oil storage facilities, bridges, hydraulic facilities, power transmission towers, cell towers, devices and equipment, as well as other metal surfaces with high requirements for hardness, strength, abrasion resistance, moisture resistance. It is characterized by good sanding, bending strength, improved adhesion, and accelerated open time.
As part of a complex coating, it is successfully used in moderate and cold climates, while providing long-term protection against corrosion.
Information on the material resistance to various media is available on request.
Main fields of application: oil and gas industry, transport construction, power engineering, tank equipment, mechanical engineering, chemical industry.Instruction for use
Metal surface should be abrasive blasted to grade 1 or 2 to GOST 9.402 (Sa 2,5 or Sa 2 to ISO8501-1:2007). Clean surface must be free from dust and grease.
If the quality of surface preparation decreases, the service life and its operating performance may change.
Conditions
Ambient temperature from +5°С to +30°C.
Relative air humidity no more 80%
The process of applying
|
Blending |
Polyurethane primer consists of two components: component А - basis, component B - hardener. Before use, pre-mix component A with a low-speed drill with mixing nozzle, then mix with component B in stoichiometric ratio in the delivery form. Mix the resulting material thoroughly until smooth. After the hardener is added into the semi-finished product, the material should be allowed to stand for at least 5-10 minutes. |
| Proportions |
Polytex ST hardener 100:10 by weight 8:1 by volume Polytex ST2 hardener 100:9 by weight 9,5:1 by volume Polytex ST2S hardener 100:22 by weight 3:1 by volume |
|
Pot life at 200С, no less |
3 hours |
| Air-free spraying |
Dilution: 5-30% The diameter of the nozzle: 0,011-0,017" Initial pressure: 120-160 ATM |
| Air spraying |
Operational viscosity:25-100 s Thinning: 5-35% Nozzle diameter:1,8-2,5 mm Initial pressure: 3,0-4,0 atm |
|
Roller Brush |
Can be recommended for small and hard-to-reach areas. Thin the primer-enamel depending on the working conditions when using brush. |
|
Thinner |
Formula thinner Polytex, RP-1K. |
|
Cleaner |
Formula thinner Polytex, RP-1K, RP-1K F, thinners of type Р4, Р5. |
|
Finishing |
Tubing, pistol and other spraying tools must be cleaned after using. |
|
Cleaning |
Clean straight after using due to painting equipment manual. |