Description
Two component polyurethane primer-enamel, hardened by aliphatic polyisocyanate.
Scope and specifics of application
Polytex 3390 HS primer enamel is used for metal structures anticorrosive protection, as well as for creating high-quality coatings distinguished by outstanding weather resistance. It has both accelerated time of complete polymerization and stable gloss.
Polytex 3390 HS is used to paint commercial vehicles (vans, buses, trolleybuses, tow trucks, garbage trucks, cars used for street washing, dumpers, car counters, trailer transformers, etc.), as well as other metal surfaces which are of high requirements both in appearance and wear resistance.
Primer-enamel is used in conditions of diverse aggressive impacts – chemical, atmospheric, mechanical, as well as in conditions of high humidity.
Information on the material resistance to various media is available on request.
Main fields of application: oil and gas industry, power engineering, capacitive equipment, mechanical engineering, chemical industry.
Instruction for use
Metal surface should be abrasive blasted to grade 1 or 2 to GOST 9.402 (Sa 2,5 or Sa 2 to ISO 8501-1:2007). Clean surface must be free from dust and grease.
If the quality of surface preparation decreases, the service life and its operating performance may change.
Conditions
Ambient temperature from +5°С to +30°C.
Relative air humidity no more 80%.
The process of applying
|
Blending |
Polyurethane primer-enamel consists of two components: component А - basis, component B - hardener. Before use, pre-mix component A with a low-speed drill with mixing nozzle, then mix with component B in stoichiometric ratio in the delivery form. Mix the resulting material thoroughly until smooth. After the hardener is added into the semi-finished product, the material should be allowed to stand for at least 5-10 minutes. |
| Proportions |
Polytex ST hardener 100:20 by weight 4,5:1 by volume Polytex ST2 hardener 100:17 by weight 5,5:1 by volume |
|
Pot life at 200С, no less |
No less than 5 hours |
| Air spraying |
Operational viscosity : 25-40 s Thinning: 5-10% Nozzle diameter:1,5-1,7 mm Initial pressure: 3-4 atm |
|
Roller Brush |
Can be recommended for small and hard-to-reach areas. Thin the primer-enamel depending on the working conditions when using brush. |
|
Thinner |
Formula thinner Polytex |
|
Cleaner |
Formula thinner Polytex, thinners of type Р4, Р5, xylene |
|
Finishing |
Tubing, pistol and other spraying tools must be cleaned after using. |
|
Cleaning |
Clean straight after using due to painting equipment manual. |